Gloss Zinc Plating Solution by Dr. Galva – Premium Corrosion Protection with High Gloss
Protect your workpieces reliably from corrosion while giving them a brilliant high-gloss finish with Dr. Galva's zinc plating solution. This powerful formula is specifically designed for both private and commercial use, offering an ideal combination of efficiency, environmental friendliness, and aesthetically pleasing results.
Your Benefits at a Glance:
-
Fast and Even Coating: The mildly acidic zinc plating solution ensures a high deposition speed with maximum current efficiency, guaranteeing an even and durable zinc layer.
-
Outstanding Gloss: Stable gloss additives provide a brilliant zinc layer, enhancing the appearance of your workpieces.
-
Environmentally Friendly: Formulated without cyanides or ammonium, this solution is eco-friendly and minimizes harmful wastewater discharges.
-
Versatile Application Options: Ideal for bath plating, barrel plating, and pen plating – even hard-to-reach areas are easy to plate.
-
Smooth, Flawless Surface: Special additives prevent the formation of dendritic zinc, ensuring a consistently smooth and flawless surface.
Application Examples:
Whether it’s screws, car body parts, or other metallic workpieces – with Dr. Galva's gloss zinc plating solution, you always achieve professional results. Perfect for iron, steel, copper, and copper alloys.
Optimized preparation for perfect results:
Thorough cleaning is crucial. Carefully remove rust and degrease your workpieces to create the ideal base for an even zinc layer.
The Galvanization Process:
Use zinc anodes for the galvanization process, and adjust the current so that only minimal gas development occurs at the workpiece. This ensures a perfect, even coating without disturbances.
Conclusion:
Dr. Galva's gloss zinc plating solution offers the ideal combination of corrosion protection, environmental compatibility, and a high-gloss finish – perfect for private and industrial use. Trust in a product that excels in quality, durability, and aesthetics.
Parameters (voltage values are indicative):
- Current density: 0.4-2.5A/dm² (up to 5A/dm² with movement)
- Bath plating: U ≈ 1.3 / 2 / 3.7 V (at 5 / 10 / 20 cm distance)
- Brush plating: U ≈ 3-7V (approx. 5V recommended)
- Working temperature: 15-60°C
- pH value: approx. 4,5
- Immersion time: 10-45min
- Deposition rate: approx. 0.6µm/min at 2A/dm² and 20°C
- Anodes: Zinc
Labeling of the mixture:
Zinc plating solution
(contains zinc sulphate, succinic acid, potassium hydroxide)
Signal word: Danger
H290 May be corrosive to metals.
H315 Causes skin irritation.
H318 Causes serious eye damage.
H411 Toxic to aquatic life with long lasting effects.
P101 If medical advice is needed, have product container or label at hand.
P102 Keep out of reach of children.
P280 Wear protective gloves and eye protection/face protection.
P302+P352 IF ON SKIN: Wash with plenty of water.
P305+P351+P338 IF IN EYES: Rinse cautiously with water for several minutes. Remove contact lenses, if present and easy to do. Continue rinsing.
P310 Immediately call a POISON CENTER/doctor.
P501 Dispose of contents/container to an appropriate recycling or disposal facility.